Description
Typical Charpy V-Notch Properties
| Impact Value | Testing Temperature | |||
| As Welded | ||||
| 70 J (52 ft-lb) | -110 degC (-166 degF) | |||
| 45 J (33 ft-lb) | -196 degC (-321 degF) | |||
| 95 J (70 ft-lb) | -60 degC (-76 degF) | |||
| 120 J (89 ft-lb) | 20 degC (68 degF) | |||
Typical Tensile Properties
| Condition | As Welded | As Welded |
| Tensile Strength | 560 MPa (81 ksi) | 400 MPa (58 ksi) |
| Yield Strength | 400 MPa (58 ksi) | 340 MPa (49 ksi) |
| Elongation | 37 % |
Recommended Welding Parameters
| Current | Voltage | Wire Diameter | Wire Feed Speed | |
| 40-120 A | 15-19 V | 0.8 mm (0.030 in.) | 4.0-8.0 m/min (157-315 in./min) | |
| 60-220 A | 15-28 V | 1.0 mm (0.040 in.) | 4.0-12.0 m/min (157-472 in./min) | |
| 150-260 A | 24-29 V | 1.2 mm (0.047 in.) | 3.0-10.0 m/min (118-394 in./min) | |
| 230-350 A | 25-30 V | 1.6 mm (1/16 in.) | 3.0-5.0 m/min (118-197 in./min) | |
Classifications
| Wire Electrode | SFA/AWS A5.9 : ER316LSi EN ISO 14343-A : G 19 12 3 L Si Werkstoffnummer : 1.4430 |
Approvals
| Approvals | CE EN 13479 DB 43.118.07 VdTÜV 02367 |
| Approvals are based on factory location. Please contact ESAB for more information. |
Consumable Characteristics
| Alloy Type | Austenitic (with appr. 8 % ferrite) 19 % Cr – 12 % Ni – 3 % Mo – Low C – High Si |
Typical Weld Metal Analysis %
| Typical Wire Composition % | ||||||||||||||
| C | Co | Cr | Cu | FN WRC-92 | Mn | Mo | N | Nb | Ni | P | S | Si | Ti | |
| <0.025 % | 0.06 % | 18.4 % | 0.13 % | 9 % | 1.7 % | 2.6 % | 0.05 % | 0.02 % | 11.7 % | <0.02 % | <0.015 % | 0.8 % | 0.01 % | |
| Typical Weld Metal Analysis % | ||||||||||||||
| 0.02 % | – | 18.5 % | 0.1 % | – | 1.8 % | 2.7 % | – | – | 12 % | 0.015 % | 0.015 % | 0.8 % | – | |