EXATON NIFECR-1

NiFeCr-1 welding wire is suitable for overlay welding when a deposit with chemistry corresponding to UNS N08825 is required. The weld deposit is a nickel-iron-chromium-molybdenum-copper alloy suitable for use in extremely corrosive environments. NiFeCr-1 has very good resistance to stress corrosion…

Category:

Description

Typical Tensile Properties

Condition Tensile Strength Yield Strength
As Welded 550 MPa (80 ksi) 340 MPa (49 ksi)

Recommended Welding Parameters

Current Voltage Wire Diameter Wire Feed Speed
60-220 A 15-28 V 1.0 mm (0.040 in.) 4.0-12.0 m/min (157-472 in./min)
150-260 A 24-29 V 1.2 mm (0.047 in.) 3.0-10.0 m/min (118-394 in./min)
230-350 A 25-30 V 1.6 mm (1/16 in.) 3.0-5.0 m/min (118-197 in./min)

Classifications

Wire Electrode SFA/AWS A5.14 : ERNiFeCr-1
EN ISO 18274 : S Ni 8065 (NiFe30Cr21Mo3)

Typical Weld Metal Analysis %

Typical Wire Composition %
C Cr Cu Fe Mn Mo Ni P S Si
<=0.025 % 23 % 2.3 % >=22.0 % 1 % 3 % >=42.0 % <=0.025 % <=0.010 % <=0.3 %