Description
Typical Tensile Properties
| Condition | As Welded | As Welded |
| Tensile Strength | 440 MPa | 610 MPa |
| Yield Strength | 290 MPa | 460 MPa |
| Elongation | 25 % | 38 % |
Recommended Welding Parameters
| Current | Voltage | Wire Diameter | Wire Feed Speed | |
| 40-120 A | 15-19 V | 0.8 mm (0.030 in.) | 4.0-8.0 m/min (157-315 in./min) | |
| 60-220 A | 15-28 V | 1.0 mm (0.040 in.) | 4.0-12.0 m/min (157-472 in./min) | |
| 150-260 A | 24-29 V | 1.2 mm (0.047 in.) | 3.0-10.0 m/min (118-394 in./min) | |
| 230-350 A | 25-30 V | 1.6 mm (1/16 in.) | 3.0-5.0 m/min (118-197 in./min) | |
Classifications
| Wire Electrode | EN ISO 14343-A : G 19 9 L SFA/AWS A5.9 : ER308L Werkstoffnummer : 1.4316 |
Approvals
| Approvals | CE EN 13479 DB 43.039.01 VdTÜV 01339 |
| Approvals are based on factory location. Please contact ESAB for more information. |
Consumable Characteristics
| Alloy Type | Austenitic (with approx. 8 % ferrite) 19% Cr – 9% Ni – Low C |
Typical Weld Metal Analysis %
| Typical Wire Composition % | ||||||||||||||
| C | Co | Cr | Cu | FN WRC-92 | Mn | Mo | N | Nb | Ni | P | S | Si | Ti | |
| 0.010 % | 0.10 % | 19.8 % | 0.2 % | 6 % | 1.8 % | 0.2 % | 0.05 % | 0.01 % | 10.8 % | 0.020 % | 0.009 % | 0.4 % | 0.003 % | |
| Typical Weld Metal Analysis % | ||||||||||||||
| 0.011 % | 0.05 % | 19.6 % | 0.15 % | 6 % | 1.9 % | 0.3 % | 0.06 % | 0.01 % | 10.1 % | 0.018 % | 0.008 % | 0.3 % | 0.003 % | |